| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | VC108 | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, yield | 98 | MPa | SABIC - Japan Method | |
| Tensile Strain, break | 3 | % | SABIC - Japan Method | |
| Flexural Stress | 148 | MPa | ASTM D790 | |
| Flexural Modulus | 5980 | MPa | ASTM D790 | |
| IMPACT | 1) | |||
| Izod Impact, notched, 23掳C | 39 | J/m | ASTM D256 | |
| THERMAL | 1) | |||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 199 | 掳C | ASTM D648 | |
| CTE, -30掳C to 30掳C | 8.00E-05 | 1/掳C | TMA | |
| PHYSICAL | 1) | |||
| Specific Gravity | 1.43 | - | ASTM D792 | |
| Water Absorption, (23掳C/24hrs) | 0.07 | % | ASTM D570 | |
| Mold Shrinkage, flow, 3.2 mm | 3) | 0.3-0.5 | % | SABIC method |
| Mold Shrinkage, flow, 6.4 mm | 3) | 0.8-1 | % | SABIC method |
| ELECTRICAL | 1) | |||
| Surface Resistivity | 4) | 1.E+08-1.E+12 | 惟 | ASTM D257 |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 120 | 掳C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 235-255 | 掳C | ||
| Nozzle Temperature | 230-250 | 掳C | ||
| Front - Zone 3 Temperature | 235-255 | 掳C | ||
| Middle - Zone 2 Temperature | 230-250 | 掳C | ||
| Rear - Zone 1 Temperature | 225-245 | 掳C | ||
| Mold Temperature | 50-130 | 掳C | ||
| Back pressure (Plastic Pressure) | 3-8 | MPa | ||
| Screw speed (Circumferential speed) | 0.1-0.2 | m/s | ||
| Shot to Cylinder Size | 30-70 | % |