PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
MECHANICAL | 1) |
|
|
|
---|
Tensile Stress, yield |
| 117 | MPa | SABIC - Japan Method |
---|
Tensile Strain, break |
| 3 | % | SABIC - Japan Method |
---|
Flexural Stress |
| 176 | MPa | ASTM D790 |
---|
Flexural Modulus |
| 7350 | MPa | ASTM D790 |
---|
IMPACT | 1) |
|
|
|
---|
Izod Impact, notched, 23掳C |
| 49 | J/m | ASTM D256 |
---|
THERMAL | 1) |
|
|
|
---|
HDT, 0.45 MPa, 3.2 mm, unannealed |
| 180 | 掳C | ASTM D648 |
---|
CTE, -30掳C to 30掳C |
| 6.00E-05 | 1/掳C | TMA |
---|
PHYSICAL | 1) |
|
|
|
---|
Specific Gravity |
| 1.44 | - | ASTM D792 |
---|
Water Absorption, (23掳C/24hrs) |
| 0.07 | % | ASTM D570 |
---|
Mold Shrinkage, flow, 3.2 mm | 3) | 0.2-0.3 | % | SABIC method |
---|
Mold Shrinkage, flow, 6.4 mm | 3) | 0.7-0.8 | % | SABIC method |
---|
ELECTRICAL | 1) |
|
|
|
---|
Surface Resistivity | 4) | 1.E+05-1.E+08 | 惟 | ASTM D257 |
---|
INJECTION MOLDING | 2) |
|
|
|
---|
Drying Temperature |
| 120 | 掳C |
|
---|
Drying Time |
| 2-4 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 235-255 | 掳C |
|
---|
Nozzle Temperature |
| 230-250 | 掳C |
|
---|
Front - Zone 3 Temperature |
| 235-255 | 掳C |
|
---|
Middle - Zone 2 Temperature |
| 230-250 | 掳C |
|
---|
Rear - Zone 1 Temperature |
| 225-245 | 掳C |
|
---|
Mold Temperature |
| 50-130 | 掳C |
|
---|
Back pressure (Plastic Pressure) |
| 3-8 | MPa |
|
---|
Screw speed (Circumferential speed) |
| 0.1-0.2 | m/s |
|
---|
Shot to Cylinder Size |
| 30-70 | % |
|
---|
1)The information stated on Technical Datasheets should be used as indicative only for material selection p