| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | ENH8560 | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, yld, Type I, 50 mm/min | 46 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 46 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 10 mm/min | 20 | % | SABIC - Japan Method | |
| Tensile Strain, brk, Type I, 10 mm/min | 20 | % | SABIC - Japan Method | |
| Tensile Modulus, 5 mm/min | 2420 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 77 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D790 | |
| IMPACT | 1) | |||
| Izod Impact, notched, 23掳C | 41 | J/m | ASTM D256 | |
| ELECTRICAL | 1) | |||
| Surface Resistivity | 4) | 9.E+12 | 惟 | ASTM D257 |
| PHYSICAL | 1) | |||
| Specific Gravity | 1.32 | - | ASTM D792 | |
| Mold Shrinkage, flow, 3.2 mm | 3) | 1.5-1.8 | % | SABIC method |
| Melt Flow Rate, 250掳C/1.2 kgf | 30 | g/10 min | ASTM D1238 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 110 | 掳C | ||
| Drying Time | 3-5 | Hrs | ||
| Melt Temperature | 230-260 | 掳C | ||
| Nozzle Temperature | 240-260 | 掳C | ||
| Front - Zone 3 Temperature | 240-260 | 掳C | ||
| Middle - Zone 2 Temperature | 230-250 | 掳C | ||
| Rear - Zone 1 Temperature | 220-240 | 掳C | ||
| Mold Temperature | 30-60 | 掳C | ||
| THERMAL | 1) | |||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 161 | 掳C | ASTM D648 |