是否进口: | 否 | 厂家(产地): | 中国 |
---|---|---|---|
牌号: | MV008SXP | 用途级别: | 注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
FLAME CHARACTERISTICS | 1) | |||
UL Yellow Card Link | E45329-101358095 | - | - | |
UL Recognized, 94HB Flame Class Rating | 1) | 1.5 | mm | UL 94 |
MECHANICAL | 2) | |||
Tensile Modulus, 5 mm/min | 10440 | MPa | ASTM D638 | |
Tensile Stress, brk, Type I, 5 mm/min | 131 | MPa | ASTM D638 | |
Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D638 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 9350 | MPa | ASTM D790 | |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D790 | |
Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 1.5 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 14000 | MPa | ISO 527 | |
Flexural Stress, break, 2 mm/min | 209 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 11700 | MPa | ISO 178 | |
IMPACT | 2) | |||
Izod Impact, notched, 23掳C | 208 | J/m | ASTM D256 | |
Instrumented Dart Impact Energy @ peak, 23掳C | 13 | J | ASTM D3763 | |
Izod Impact, unnotched 80*10*4 +23掳C | 55 | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 27 | kJ/m虏 | ISO 180/1A | |
Multiaxial Impact | 13 | J | ISO 6603 | |
THERMAL | 2) | |||
HDT, 1.82 MPa, 3.2mm, unannealed | 157 | 掳C | ASTM D648 | |
CTE, -40掳C to 40掳C, flow | 3.4E-05 | 1/掳C | ASTM E831 | |
CTE, -40掳C to 40掳C, xflow | 4.6E-05 | 1/掳C | ASTM E831 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 164 | 掳C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 159 | 掳C | ISO 75/Af | |
CTE, -40掳C to 40掳C, flow | 3.4E-05 | 1/掳C | ISO 11359-2 | |
CTE, -40掳C to 40掳C, xflow | 4.6E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 60掳C, flow | 3.4E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 60掳C, xflow | 4.6E-05 | 1/掳C | ISO 11359-2 | |
PHYSICAL | 2) | |||
Density | 1.33 | g/cm鲁 | ASTM D792 | |
Wear Factor Washer | 73 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual | |
Dynamic COF | 0.34 | - | ASTM D3702 Modified: Manual | |
Static COF | 0.52 | - | ASTM D3702 Modified: Manual | |
Density | 1.33 | g/cm鲁 | ISO 1183 | |
INJECTION MOLDING | 3) | |||
Drying Temperature | 80 | 掳C | ||
Drying Time | 4 | Hrs | ||
Melt Temperature | 220-250 | 掳C | ||
Front - Zone 3 Temperature | 250-260 | 掳C | ||
Middle - Zone 2 Temperature | 245-255 | 掳C | ||
Rear - Zone 1 Temperature | 230-245 | 掳C | ||
Mold Temperature | 40-65 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm |