是否进口: | 否 | 厂家(产地): | 中国 |
---|---|---|---|
牌号: | MVL36SX0 | 用途级别: | 注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | 1) | |||
Tensile Stress, break, 5 mm/min | 116 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 2.2 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 8500 | MPa | ISO 527 | |
Flexural Stress, break, 2 mm/min | 133 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 | |
IMPACT | 1) | |||
Multiaxial Impact | 5 | J | ISO 6603 | |
Izod Impact, unnotched 80*10*4 +23掳C | 42 | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 17 | kJ/m虏 | ISO 180/1A | |
THERMAL | 1) | |||
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 163 | 掳C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 157 | 掳C | ISO 75/Af | |
PHYSICAL | 1) | |||
Mold Shrinkage, flow, 24 hrs | 3) | 0.37 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 3) | 0.73 | % | ISO 294 |
Density | 1.28 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/24hrs) | 0.01 | % | ISO 62-1 | |
INJECTION MOLDING | 2) | |||
Drying Temperature | 80 | 掳C | ||
Drying Time | 4 | Hrs | ||
Melt Temperature | 215-220 | 掳C | ||
Front - Zone 3 Temperature | 205-215 | 掳C | ||
Middle - Zone 2 Temperature | 200-210 | 掳C | ||
Rear - Zone 1 Temperature | 195-205 | 掳C | ||
Mold Temperature | 30-50 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm |