| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | MV00CS | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 1.2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 15100 | MPa | ISO 527 | |
| Flexural Modulus, 2 mm/min | 13700 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 | |
| Tensile Modulus, 5 mm/min | 17300 | MPa | ASTM D638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 1.1 | % | ASTM D638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D638 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13800 | MPa | ASTM D790 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 135 | MPa | ASTM D790 | |
| IMPACT | 1) | |||
| Izod Impact, notched 80*10*4 +23掳C | 14 | kJ/m虏 | ISO 180/1A | |
| Izod Impact, unnotched 80*10*4 +23掳C | 39 | kJ/m虏 | ISO 180/1U | |
| Charpy 23掳C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m虏 | ISO 179/1eA | |
| Charpy 23掳C, Unnotch Edgew 80*10*4 sp=62mm | 29 | kJ/m虏 | ISO 179/1eU | |
| Izod Impact, notched, 23掳C | 155 | J/m | ASTM D256 | |
| Izod Impact, unnotched, 23掳C | 620 | J/m | ASTM D4812 | |
| THERMAL | 1) | |||
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 154 | 掳C | ISO 75/Af | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 160 | 掳C | ISO 75/Bf | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 156 | 掳C | ASTM D648 | |
| PHYSICAL | 1) | |||
| Density | 1.47 | g/cm鲁 | ISO 1183 | |
| Moisture Absorption (23掳C / 50% RH) | 0.04 | % | ISO 62 | |
| Mold Shrinkage, flow, 24 hrs | 3) | 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 3) | 0.8 | % | ASTM D955 |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Melt Temperature | 220-250 | 掳C | ||
| Front - Zone 3 Temperature | 250-260 | 掳C | ||
| Middle - Zone 2 Temperature | 245-255 | 掳C | ||
| Rear - Zone 1 Temperature | 230-245 | 掳C | ||
| Mold Temperature | 40-65 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |