XENOY X2500UV is a medium viscosity, unfilled, UV stabilized, elastomer modified PC/PET blend with excellent heat and impact performance. ***1043-label: PC+PET-I.Europe
下载文件技术数据
比较
EUROPE
| Revision: 07/08/2018 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yield | 53 | MPa | ASTM D638 | |
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 | |
| Tensile Strain, yield | 5 | % | ASTM D638 | |
| Tensile Strain, break | 100 | % | ASTM D638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 80 | % | ASTM D638 | |
| Tensile Modulus, 50 mm/min | 2200 | MPa | ASTM D638 | |
| Flexural Stress | 79 | MPa | ASTM D790 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 79 | MPa | ASTM D790 | |
| Flexural Modulus | 2100 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2150 | MPa | ASTM D790 | |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 50 mm/min | 57 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 56 | MPa | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 70 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2200 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2150 | MPa | *** 178 | |
| Ball Indentation Hardness, H358/30 | 95 | MPa | *** 2039-1 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 600 | J/m | ASTM D256 | |
| Izod Impact, notched, 0°C | 450 | J/m | ASTM D256 | |
| Izod Impact, notched, -30°C | 200 | J/m | ASTM D256 | |
| Instrumented Dart Impact Total Energy, 23°C | 60 | J | ASTM D3763 | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m? | *** 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 30 | kJ/m? | *** 179/1eA | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 135 | °C | ASTM D1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 108 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 8.5E-05 | 1/°C | ASTM E831 | |
| Thermal Conductivity | 0.18 | W/m-°C | *** 8302 | |
| CTE, 23°C to 80°C, flow | 8.2E-05 | 1/°C | *** 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.7E-05 | 1/°C | *** 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 145 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/50 | 135 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 136 | °C | *** 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 108 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.21 | - | ASTM D792 | |
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 265°C/2.16kgf | 9 | g/10 min | ASTM D1238 | |
| Density | 1.21 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.7 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | *** 62 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 4 | cm?/10 min | *** 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+14 | Ω.cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.5 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 2.7 | mm | IEC 60695-2-12 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 265 - 275 | °C | ||
| Nozzle Temperature | 260 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 250 - 275 | °C | ||
| Rear - Zone 1 Temperature | 240 - 270 | °C | ||
| Hopper Temperature | 60 - 80 | °C | ||
| Mold Temperature | 60 - 100 | °C |