XENOY X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4830 could be positioned for body panels, safety equipment, housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment.EuropeAsia
下载文件技术数据
比较
EUROPE
ASIA
| Revision: 23/10/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 60 | MPa | ASTM D638 | |
| Tensile Stress, yld, Type I, 5 mm/min | 56 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 60 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 4.1 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 140 | % | ASTM D638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 4.5 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 150 | % | ASTM D638 | |
| Tensile Modulus, 5 mm/min | 3400 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3100 | MPa | ASTM D790 | |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 55 | MPa | *** 527 | |
| Tensile Stress, break, 5 mm/min | 60 | MPa | *** 527 | |
| Tensile Stress, yield, 50 mm/min | 61 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 55 | MPa | *** 527 | |
| Tensile Strain, yield, 5 mm/min | 4.1 | % | *** 527 | |
| Tensile Strain, break, 5 mm/min | 120 | % | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 4.2 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 110 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 3200 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2900 | MPa | *** 178 | |
| Ball Indentation Hardness, H358/30 | 105 | MPa | *** 2039-1 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 600 | J/m | ASTM D256 | |
| Izod Impact, notched, 0°C | 150 | J/m | ASTM D256 | |
| Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 | |
| Multiaxial Impact | 110 | J | *** 6603 | |
| Instrumented Dart Impact Total Energy, 23°C | 70 | J | ASTM D3763 | |
| Instrumented Impact Total Energy, -20°C | 70 | J | ASTM D3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 15 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 40 | kJ/m? | *** 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m? | *** 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 133 | °C | ASTM D1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 125 | °C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 8.2E-05 | 1/°C | ASTM E831 | |
| Thermal Conductivity | 0.2 | W/m-°C | *** 8302 | |
| CTE, -30°C to 80°C, flow | 7.2E-05 | 1/°C | *** 11359-2 | |
| CTE, -30°C to 80°C, xflow | 9.E-05 | 1/°C | *** 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 133 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 135 | °C | *** 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 119 | °C | *** 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 97 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.27 | - | ASTM D792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.7-0.9 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 7 | g/10 min | ASTM D1238 | |
| Density | 1.27 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.42 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | *** 62 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 6 | cm?/10 min | *** 1133 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-100 | °C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 255-270 | °C | ||
| Nozzle Temperature | 250-265 | °C | ||
| Front - Zone 3 Temperature | 250-270 | °C | ||
| Middle - Zone 2 Temperature | 240-265 | °C | ||
| Rear - Zone 1 Temperature | 230-250 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-80 | °C |