Mineral filled PC/PET blend with high flow, high heat, dimensional stability, low shrinkage and low CTE, especially for painted applicationsEuropeAmericas
下载文件技术数据
比较
EUROPE
AMERICAS
| Revision: 06/08/2020 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yield, 5 mm/min | 58 | MPa | *** 527 | |
| Tensile Stress, break, 5 mm/min | 42 | MPa | *** 527 | |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | *** 527 | |
| Tensile Strain, break, 5 mm/min | 9 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 3850 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 3750 | MPa | *** 178 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m? | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 120 | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m? | *** 179/1eA | |
| THERMAL | ||||
| CTE, -30°C to 80°C, flow | 5.4E-05 | 1/°C | *** 11359-2 | |
| CTE, -30°C to 80°C, xflow | 7.4E-05 | 1/°C | *** 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 137 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 140 | °C | *** 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 109 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 265°C/5.0 kgf | 28 | g/10 min | ASTM D1238 | |
| Density | 1.33 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.42 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | *** 62 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 24 | cm?/10 min | *** 1133 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 4-6 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 265-275 | °C | ||
| Nozzle Temperature | 260-275 | °C | ||
| Front - Zone 3 Temperature | 260-280 | °C | ||
| Middle - Zone 2 Temperature | 250-275 | °C | ||
| Rear - Zone 1 Temperature | 240-270 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 60-100 | °C |