Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (***10993 or USP Class VI). EtO, Gamma and Steam sterilizable.AsiaAmericas
下载文件技术数据
比较
ASIA
AMERICAS
| Revision: 07/08/2018 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 50 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 52 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D638 | |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 70 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2000 | MPa | ASTM D790 | |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 55 | MPa | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 100 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2050 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 75 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2050 | MPa | *** 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 750 | J/m | ASTM D256 | |
| Izod Impact, notched, -30°C | 600 | J/m | ASTM D256 | |
| Instrumented Dart Impact Total Energy, 23°C | 80 | J | ASTM D3763 | |
| Izod Impact, unnotched 80*10*4 -40°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 55 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m? | *** 180/1A | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 60 | kJ/m? | *** 179/1eA | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 125 | °C | ASTM D1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 9.E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | *** 11359-2 | |
| CTE, -40°C to 40°C, xflow | 9.E-05 | 1/°C | *** 11359-2 | |
| CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | *** 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 125 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 123 | °C | *** 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 105 | °C | *** 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.22 | - | ASTM D792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.7-1.1 | % | SABIC method | |
| Melt Flow Rate, 250°C/5.0 kgf | 11 | g/10 min | ASTM D1238 | |
| Density | 1.22 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.4 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | *** 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 10 | cm?/10 min | *** 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 260 | Pa-s | *** 11443 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-100 | °C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 255-270 | °C | ||
| Nozzle Temperature | 250-265 | °C | ||
| Front - Zone 3 Temperature | 250-270 | °C | ||
| Middle - Zone 2 Temperature | 240-265 | °C | ||
| Rear - Zone 1 Temperature | 230-250 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-80 | °C |