CL101
Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applications. ***1043: PC+PBT-I.EuropeAsiaAmericas
下载文件技术数据
比较
EUROPE
ASIA
AMERICAS
| Revision: 03/10/2023 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 49 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 4.5 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 | |
| Tensile Modulus, 50 mm/min | 2050 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 75 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2000 | MPa | ASTM D790 | |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 50 mm/min | 52 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 44 | MPa | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 100 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2050 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 75 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | *** 178 | |
| Ball Indentation Hardness, H358/30 | 82 | MPa | *** 2039-1 | |
| Hardness, Rockwell L | 89 | - | *** 2039-2 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 625 | J/m | ASTM D256 | |
| Izod Impact, notched, 0°C | 600 | J/m | ASTM D256 | |
| Izod Impact, notched, -30°C | 450 | J/m | ASTM D256 | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 35 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 25 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m? | *** 179/1eA | |
| Charpy Impact, notched, 23°C | 30 | kJ/m? | *** 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 25 | kJ/m? | *** 179/1eA | |
| Charpy Impact, notched, -20°C | 25 | kJ/m? | *** 179/2C | |
| Charpy Impact, notched, -30°C | 20 | kJ/m? | *** 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 120 | °C | ASTM D1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 83 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ASTM E831 | |
| Thermal Conductivity | 0.18 | W/m-°C | *** 8302 | |
| CTE, 23°C to 80°C, flow | 9.E-05 | 1/°C | *** 11359-2 | |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | *** 11359-2 | |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 155 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/50 | 120 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 123 | °C | *** 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 105 | °C | *** 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 83 | °C | *** 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 105 | °C | *** 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 83 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.22 | - | ASTM D792 | |
| Mold Shrinkage on Tensile Bar, flow | 0.7-1.1 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.7-1.1 | % | SABIC method | |
| Melt Flow Rate, 250°C/5.0 kgf | 14 | g/10 min | ASTM D1238 | |
| Density | 1.22 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.5 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | *** 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 13 | cm?/10 min | *** 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+14 | Ω.cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 | |
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.5 | mm | UL 94 by SABIC-IP | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-100 | °C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 255-270 | °C | ||
| Nozzle Temperature | 250-265 | °C | ||
| Front - Zone 3 Temperature | 250-270 | °C | ||
| Middle - Zone 2 Temperature | 240-265 | °C | ||
| Rear - Zone 1 Temperature | 230-250 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-80 | °C |