| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | RX10409D | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 2) | |||
| Tensile Stress, yield | 257 | MPa | ASTM D638 | |
| Tensile Stress, break | 257 | MPa | ASTM D638 | |
| Tensile Strain, yield | 1.8 | % | ASTM D638 | |
| Tensile Strain, break | 1.8 | % | ASTM D638 | |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D638 | |
| Flexural Stress | 386 | MPa | ASTM D790 | |
| Flexural Modulus | 17230 | MPa | ASTM D790 | |
| Tensile Stress, yield | 222 | MPa | ISO 527 | |
| Tensile Stress, break | 222 | MPa | ISO 527 | |
| Tensile Strain, yield | 1.4 | % | ISO 527 | |
| Tensile Strain, break | 1.4 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 19220 | MPa | ISO 527 | |
| Flexural Stress | 393 | MPa | ISO 178 | |
| Flexural Modulus | 17000 | MPa | ISO 178 | |
| IMPACT | 2) | |||
| Izod Impact, unnotched, 23掳C | 1228 | J/m | ASTM D4812 | |
| Izod Impact, notched, 23掳C | 267 | J/m | ASTM D256 | |
| Instrumented Dart Impact Energy @ peak, 23掳C | 9 | J | ASTM D3763 | |
| Multiaxial Impact | 7 | J | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23掳C | 78 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 41 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 2) | |||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 291 | 掳C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 266 | 掳C | ASTM D648 | |
| CTE, -40掳C to 40掳C, flow | 1.44E-05 | 1/掳C | ASTM E831 | |
| CTE, -40掳C to 40掳C, xflow | 3.06E-05 | 1/掳C | ASTM E831 | |
| CTE, -40掳C to 40掳C, flow | 1.50E-05 | 1/掳C | ISO 11359-2 | |
| CTE, -40掳C to 40掳C, xflow | 3.10E-05 | 1/掳C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 296 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 272 | 掳C | ISO 75/Af | |
| PHYSICAL | 2) | |||
| Density | 1.67 | g/cm鲁 | ASTM D792 | |
| Moisture Absorption, (23掳C/50% RH/24 hrs) | 0.2 | % | ASTM D570 | |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 | |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D955 | |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs | 0.48 | % | ISO 294 | |
| Density | 1.66 | g/cm鲁 | ISO 1183 | |
| INJECTION MOLDING | 3) | |||
| Drying Temperature | 120-150 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15 | % | ||
| Melt Temperature | 315-330 | 掳C | ||
| Front - Zone 3 Temperature | 330-345 | 掳C | ||
| Middle - Zone 2 Temperature | 320-330 | 掳C | ||
| Rear - Zone 1 Temperature | 315-325 | 掳C | ||
| Mold Temperature | 140-165 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |