| 牌号： | WV006 | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break | 187 | MPa | ISO 527 | |
| Tensile Strain, break | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 11570 | MPa | ISO 527 | |
| Flexural Stress | 247 | MPa | ISO 178 | |
| Flexural Modulus | 9780 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched 80*10*4 +23掳C | 56 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 30 | kJ/m虏 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40掳C | 36 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 1) | |||
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 225 | 掳C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Density | 1.54 | g/cm鲁 | ISO 1183 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 120 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.05 | % | ||
| Melt Temperature | 250-260 | 掳C | ||
| Front - Zone 3 Temperature | 250-260 | 掳C | ||
| Middle - Zone 2 Temperature | 240-250 | 掳C | ||
| Rear - Zone 1 Temperature | 230-245 | 掳C | ||
| Mold Temperature | 65-120 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-70 | rpm |