| 牌号： | RV00CE | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break, 5 mm/min | 270 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 21600 | MPa | ISO 527 | |
| Flexural Stress, break, 2 mm/min | 430 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2.6 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 19000 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched 80*10*4 +23掳C | 100 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 53 | kJ/m虏 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40掳C | 43 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 1) | |||
| CTE, 23掳C to 60掳C, flow | 1.7E-05 | 1/掳C | ISO 11359-2 | |
| CTE, 23掳C to 60掳C, xflow | 5.3E-05 | 1/掳C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 255 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 252 | 掳C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Mold Shrinkage, flow | 3) | 0.26 | % | SABIC method |
| Mold Shrinkage, xflow | 3) | 0.61 | % | SABIC method |
| Density | 1.71 | g/cm鲁 | ISO 1183 | |
| Water Absorption, (23掳C/24hrs) | 0.9 | % | ISO 62-1 | |
| Moisture Absorption (23掳C / 50% RH) | 1.1 | % | ISO 62 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 290-305 | 掳C | ||
| Front - Zone 3 Temperature | 290-300 | 掳C | ||
| Middle - Zone 2 Temperature | 290-300 | 掳C | ||
| Rear - Zone 1 Temperature | 280-295 | 掳C | ||
| Mold Temperature | 95-110 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |