牌号: | RVL29 | 用途级别: | 注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | 1) | |||
Tensile Stress, break, 5 mm/min | 231 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 361 | MPa | ISO 178 | |
Flexural Strain, break, 2 mm/min | 3.2 | % | ISO 178 | |
Flexural Modulus, 2 mm/min | 13600 | MPa | ISO 178 | |
Flexural Strain, break, 2 mm/min, 60掳C | 3.6 | % | ISO 178 | |
Flexural Strain, break, 2 mm/min, 100掳C | 3.2 | % | ISO 178 | |
Flexural Strain, break, 2 mm/min, 150掳C | 3.5 | % | ISO 178 | |
Flexural Strain, break, 2 mm/min, 200掳C | 2.7 | % | ISO 178 | |
Flexural Stress, yield, 2 mm/min, 60掳C | 300 | MPa | ISO 178 | |
Flexural Stress, yield, 2 mm/min, 100掳C | 256 | MPa | ISO 178 | |
Flexural Stress, yield, 2 mm/min, 150掳C | 204 | MPa | ISO 178 | |
Flexural Stress, yield, 2 mm/min, 200掳C | 162 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min, 60掳C | 11700 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min, 100掳C | 10500 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min, 150掳C | 9000 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min, 200掳C | 8900 | MPa | ISO 178 | |
IMPACT | 1) | |||
Izod Impact, notched 80*10*3 -40掳C | 28 | kJ/m虏 | ISO 180/1A | |
Izod Impact, unnotched 80*10*4 +23掳C | 82 | kJ/m虏 | ISO 180/1U | |
Izod Impact, unnotched 80*10*4 -40掳C | 74 | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 30 | kJ/m虏 | ISO 180/1A | |
THERMAL | 1) | |||
Specific Heat | 1478 | J/kg-K | ASTM E1269 | |
CTE, 23掳C to 60掳C, flow | 2.1E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 60掳C, xflow | 4.9E-05 | 1/掳C | ISO 11359-2 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 258 | 掳C | ISO 75/Af | |
Thermal Conductivity | 0.27 | W/m-K | ASTM D5930 | |
PHYSICAL | 1) | |||
Mold Shrinkage, flow, 24 hrs | 3) | 0.13 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 3) | 0.48 | % | ISO 294 |
Wear Factor Washer | 21 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual | |
Dynamic COF | 0.39 | - | ASTM D3702 Modified: Manual | |
Static COF | 0.4 | - | ASTM D3702 Modified: Manual | |
Density | 1.65 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/24hrs) | 1.19 | % | ISO 62-1 | |
Moisture Absorption (23掳C / 50% RH) | 0.46 | % | ISO 62 | |
INJECTION MOLDING | 2) | |||
Drying Temperature | 80 | 掳C | ||
Drying Time | 4 | Hrs | ||
Maximum Moisture Content | 0.15-0.25 | % | ||
Melt Temperature | 290-305 | 掳C | ||
Front - Zone 3 Temperature | 290-300 | 掳C | ||
Middle - Zone 2 Temperature | 290-300 | 掳C | ||
Rear - Zone 1 Temperature | 280-295 | 掳C | ||
Mold Temperature | 95-110 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm |