是否进口: | 否 | 厂家(产地): | 中国 |
---|---|---|---|
牌号: | RVL29U | 用途级别: | 注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | 1) | |||
Tensile Modulus, 1 mm/min | 16000 | MPa | ISO 527 | |
Tensile Stress, break, 5 mm/min | 230 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
Flexural Modulus, 2 mm/min | 13000 | MPa | ISO 178 | |
Flexural Strength, 2 mm/min | 330 | MPa | ISO 178 | |
Hardness, Rockwell R | 115 | - | ISO 2039-2 | |
Hardness, Rockwell M | 112 | - | ISO 2039-2 | |
Hardness, Rockwell L | 96 | - | ISO 2039-2 | |
Tensile Modulus, 5 mm/min | 16000 | MPa | ASTM D638 | |
Tensile Stress, brk, Type I, 5 mm/min | 220 | MPa | ASTM D638 | |
Tensile Strain, brk, Type I, 5 mm/min | 2.8 | % | ASTM D638 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 12800 | MPa | ASTM D790 | |
Flexural Strength, 1.3 mm/min, 50 mm span | 320 | MPa | ASTM D790 | |
INJECTION MOLDING | 2) | |||
Drying Temperature | 80 | 掳C | ||
Drying Time | 4 | Hrs | ||
Drying Time (Cumulative) | 48 | Hrs | ||
Maximum Moisture Content | 0.15-0.25 | % | ||
Hopper Temperature | 40 | 掳C | ||
Melt Temperature | 290-305 | 掳C | ||
Rear - Zone 1 Temperature | 280-295 | 掳C | ||
Middle - Zone 2 Temperature | 290-300 | 掳C | ||
Front - Zone 3 Temperature | 290-300 | 掳C | ||
Nozzle Temperature | 290-305 | 掳C | ||
Mold Temperature | 95-110 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm | ||
PHYSICAL | 1) | |||
Density | 1.64 | g/cm鲁 | ISO 1183 | |
Moisture Absorption, (23掳C/50% RH/24hrs) | 0.4-0.6 | % | ISO 62-4 | |
Water Absorption, (23掳C/saturated) | 3.2-3.8 | % | ISO 62-1 | |
Specific Gravity | 1.66 | - | ASTM D792 | |
Wear Factor Washer | 25 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Instr. | |
Dynamic COF | 0.42 | - | ASTM D3702 Modified: Instr. | |
Static COF | 0.48 | - | ASTM D3702 Modified: Instr. | |
Mold Shrinkage, flow | 3) | 0.2-0.4 | % | SABIC method |
Mold Shrinkage, xflow | 3) | 0.7-0.9 | % | SABIC method |
THERMAL | 1) | |||
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 255 | 掳C | ISO 75/Af | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 260 | 掳C | ISO 75/Bf | |
Vicat Softening Temp, Rate B/50 | 247 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 253 | 掳C | ISO 306 | |
CTE, -40掳C to 40掳C, flow | 1.4E-05 | 1/掳C | ISO 11359-2 | |
CTE, -40掳C to 40掳C, xflow | 6.0E-05 | 1/掳C | ISO 11359-2 | |
IMPACT | 1) | |||
Izod Impact, notched 80*10*4 +23掳C | 27 | kJ/m虏 | ISO 180/1A | |
Izod Impact, notched 80*10*4 -40掳C | 27 | kJ/m虏 | ISO 180/1A | |
Izod Impact, unnotched 80*10*4 +23掳C | 81 | kJ/m虏 | ISO 180/1U | |
Izod Impact, unnotched 80*10*4 -40掳C | 76 | kJ/m虏 | ISO 180/1U | |
Charpy 23掳C, V-notch Edgew 80*10*4 sp=62mm | 31 | kJ/m虏 | ISO 179/1eA | |
Charpy 23掳C, Unnotch Edgew 80*10*4 sp=62mm | 80 | kJ/m虏 | ISO 179/1eU | |
Multi-Axial Instrumented Impact Total Energy, 23掳C | 12 | J | ISO 6603-2 | |
Izod Impact, notched, 23掳C | 170 | J/m | ASTM D256 | |
Izod Impact, unnotched, 23掳C | 1090 | J/m | ASTM D4812 | |
Instrumented Dart Impact Total Energy, 23掳C | 10 | J | ASTM D3763 |