| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | PX06418 | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, brk, Type I, 5 mm/min | 203 | MPa | ASTM D638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 | |
| Tensile Modulus, 5 mm/min | 11960 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 309 | MPa | ASTM D790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 307 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 10000 | MPa | ASTM D790 | |
| Tensile Stress, yield, 5 mm/min | 193 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 182 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10900 | MPa | ISO 527 | |
| Flexural Strength, 2 mm/min | 290 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 9530 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched, 23掳C | 1040 | J/m | ASTM D4812 | |
| Izod Impact, notched, 23掳C | 284 | J/m | ASTM D256 | |
| Multiaxial Impact | 5 | J | ISO 6603 | |
| Instrumented Dart Impact Total Energy, 23掳C | 15 | J | ASTM D3763 | |
| Izod Impact, unnotched 80*10*4 +23掳C | 64 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 27 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 1) | |||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 213 | 掳C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 208 | 掳C | ASTM D648 | |
| CTE, -30掳C to 30掳C, flow | 4.8E-05 | 1/掳C | ASTM D696 | |
| CTE, -30掳C to 30掳C, xflow | 1.1E-04 | 1/掳C | ASTM D696 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 213 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 207 | 掳C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Specific Gravity | 1.41 | - | ASTM D792 | |
| Density | 1.4 | g/cm鲁 | ASTM D792 | |
| Moisture Absorption, (23掳C/50% RH/24 hrs) | 1.1 | % | ASTM D570 | |
| Mold Shrinkage, flow, 24 hrs | 3) | 0.1-0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 3) | 0.4-0.6 | % | ASTM D955 |
| Moisture Absorption (23掳C / 50% RH) | 1.7 | % | ISO 62 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 265-275 | 掳C | ||
| Front - Zone 3 Temperature | 275-290 | 掳C | ||
| Middle - Zone 2 Temperature | 265-275 | 掳C | ||
| Rear - Zone 1 Temperature | 250-260 | 掳C | ||
| Mold Temperature | 80-95 | 掳C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 30-60 | rpm |