是否进口: | 否 | 厂家(产地): | 中国 |
---|---|---|---|
牌号: | WF003I | 用途级别: | 注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | 1) | |||
Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 3.3 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 5000 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 133 | MPa | ISO 178 | |
Flexural Stress, break, 2 mm/min | 119 | MPa | ISO 178 | |
Flexural Strain, break, 2 mm/min | 5.7 | % | ISO 178 | |
Flexural Modulus, 2 mm/min | 4350 | MPa | ISO 178 | |
IMPACT | 1) | |||
Izod Impact, unnotched 80*10*4 +23掳C | 46 | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 11 | kJ/m虏 | ISO 180/1A | |
THERMAL | 1) | |||
CTE, 23掳C to 60掳C, flow | 4.1E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 60掳C, xflow | 1.4E-04 | 1/掳C | ISO 11359-2 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 209 | 掳C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 180 | 掳C | ISO 75/Af | |
PHYSICAL | 1) | |||
Mold Shrinkage, flow | 3) | 0.4-0.7 | % | SABIC method |
Density | 1.37 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/24hrs) | 0.11 | % | ISO 62-1 | |
INJECTION MOLDING | 2) | |||
Drying Temperature | 120 | 掳C | ||
Drying Time | 4 | Hrs | ||
Maximum Moisture Content | 0.05 | % | ||
Melt Temperature | 240-265 | 掳C | ||
Front - Zone 3 Temperature | 260-270 | 掳C | ||
Middle - Zone 2 Temperature | 245-255 | 掳C | ||
Rear - Zone 1 Temperature | 220-230 | 掳C | ||
Mold Temperature | 80-100 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm |