| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | WF006I | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, yld, Type I, 5 mm/min | 64 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 55 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.4 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 4.4 | % | ASTM D638 | |
| Tensile Modulus, 5 mm/min | 3770 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 102 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3320 | MPa | ASTM D790 | |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.4 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 4.3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3670 | MPa | ISO 527 | |
| Flexural Stress | 102 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3270 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched, 23掳C | 708 | J/m | ASTM D4812 | |
| Izod Impact, notched, 23掳C | 125 | J/m | ASTM D256 | |
| Multiaxial Impact | 1 | J | ISO 6603 | |
| Instrumented Dart Impact Total Energy, 23掳C | 6 | J | ASTM D3763 | |
| Izod Impact, unnotched 80*10*4 +23掳C | 39 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 11 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 1) | |||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 214 | 掳C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 178 | 掳C | ASTM D648 | |
| CTE, -30掳C to 30掳C, flow | 7.2E-05 | 1/掳C | ASTM D696 | |
| CTE, -30掳C to 30掳C, xflow | 1.11E-04 | 1/掳C | ASTM D696 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 207 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 161 | 掳C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Specific Gravity | 1.32 | - | ASTM D792 | |
| Density | 1.32 | g/cm鲁 | ASTM D792 | |
| Moisture Absorption, (23掳C/50% RH/24 hrs) | 0.07 | % | ASTM D570 | |
| Mold Shrinkage, flow, 24 hrs | 3) | 1-1.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 3) | 1.4-1.8 | % | ASTM D955 |
| Moisture Absorption (23掳C / 50% RH) | 0.1 | % | ISO 62 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 120 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.05 | % | ||
| Melt Temperature | 240-265 | 掳C | ||
| Front - Zone 3 Temperature | 260-270 | 掳C | ||
| Middle - Zone 2 Temperature | 245-255 | 掳C | ||
| Rear - Zone 1 Temperature | 220-230 | 掳C | ||
| Mold Temperature | 80-100 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |
我公司长期提供【LNP THERMOTUF WF006I 含10%玻璃纤维的PBT树脂】，如果您对我们的【LNP THERMOTUF WF006I 含10%玻璃纤维的PBT树脂】感兴趣，请随时拨打下方的电话，点击留言或QQ与我交谈。联系我时，请说明是在供应商网上看到的，谢谢！