| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | WF006I | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, yield, 5 mm/min | 82 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 101 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7600 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 7000 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched 80*10*4 +23掳C | 55 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 13 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 1) | |||
| CTE, 23掳C to 60掳C, flow | 2.6E-05 | 1/掳C | ISO 11359-2 | |
| CTE, 23掳C to 60掳C, xflow | 1.23E-04 | 1/掳C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 218 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | 掳C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Mold Shrinkage on Tensile Bar, flow | 3) | 0.2-0.4 | % | SABIC method |
| Density | 1.47 | g/cm鲁 | ISO 1183 |