XENOY XL1562 is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties.Europe
下载文件技术数据
比较
EUROPE
| Revision: 07/08/2018 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 50 mm/min | 54 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 42 | MPa | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 100 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2100 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 74 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | *** 178 | |
| Ball Indentation Hardness, H358/30 | 100 | MPa | *** 2039-1 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 18 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m? | *** 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m? | *** 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| THERMAL | ||||
| Thermal Conductivity | 0.18 | W/m-°C | *** 8302 | |
| CTE, 23°C to 80°C, flow | 1.1E-04 | 1/°C | *** 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.1E-04 | 1/°C | *** 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 190 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/50 | 125 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 128 | °C | *** 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 110 | °C | *** 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 80 | °C | *** 75/Ae | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.8-1.1 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.8-1.1 | % | SABIC method | |
| Density | 1.23 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.5 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | *** 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 9 | cm?/10 min | *** 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 27 | cm?/10 min | *** 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+14 | Ω.cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 32 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90 - 100 | °C | ||
| Drying Time | 2 - 4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 255 - 270 | °C | ||
| Nozzle Temperature | 250 - 265 | °C | ||
| Front - Zone 3 Temperature | 250 - 270 | °C | ||
| Middle - Zone 2 Temperature | 240 - 265 | °C | ||
| Rear - Zone 1 Temperature | 230 - 250 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 80 | °C |