| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | RV0079SS | 用途级别： | 注塑 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| FLAME CHARACTERISTICS | 1) | |||
| UL Yellow Card Link | E45329-101281605 | - | - | |
| UL Recognized, 94V-0 Flame Class Rating | 鈮�1.7 | mm | UL 94 | |
| MECHANICAL | 2) | |||
| Tensile Stress, break | 213 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 213 | MPa | ISO 527 | |
| Tensile Strain, break | 1.8 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 15070 | MPa | ISO 527 | |
| Flexural Stress | 298 | MPa | ISO 178 | |
| Flexural Stress, yield, 2 mm/min | 298 | MPa | ISO 178 | |
| Flexural Modulus | 13280 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 13280 | MPa | ISO 178 | |
| IMPACT | 2) | |||
| Izod Impact, unnotched 80*10*4 +23掳C | 57 | kJ/m虏 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 32 | kJ/m虏 | ISO 180/1A | |
| THERMAL | 2) | |||
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 262 | 掳C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 259 | 掳C | ISO 75/Af | |
| Relative Temp Index, Elec | 1) | 130 | 掳C | UL 746B |
| Relative Temp Index, Mech w/impact | 1) | 105 | 掳C | UL 746B |
| Relative Temp Index, Mech w/o impact | 1) | 115 | 掳C | UL 746B |
| PHYSICAL | 2) | |||
| Density | 1.69 | g/cm鲁 | ISO 1183 | |
| ELECTRICAL | 1) | |||
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| Hot-Wire Ignition (HWI), PLC 0 | 鈮�3 | mm | UL 746A | |
| Hot-Wire Ignition (HWI), PLC 1 | 鈮�1.7 | mm | UL 746A | |
| High Amp Arc Ignition (HAI), PLC 0 | 鈮�3 | mm | UL 746A | |
| High Amp Arc Ignition (HAI), PLC 1 | 鈮�1.7 | mm | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 | |
| INJECTION MOLDING | 3) | |||
| Drying Temperature | 80 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 290-305 | 掳C | ||
| Front - Zone 3 Temperature | 290-300 | 掳C | ||
| Middle - Zone 2 Temperature | 290-300 | 掳C | ||
| Rear - Zone 1 Temperature | 280-295 | 掳C | ||
| Mold Temperature | 95-110 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |