| 是否进口： | 否 | 厂家(产地)： | 中国 |
|---|---|---|---|
| 牌号： | HC1104HF | 类型： | 标准料 |
High heat PC/ABS blend offering good flow and excellent impact.Americas
下载文件技术数据
比较
AMERICAS
| Revision: 07/08/2018 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 45 | MPa | ASTM D638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 4.8 | % | ASTM D638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 93 | % | ASTM D638 | |
| Tensile Modulus, 50 mm/min | 2250 | MPa | ASTM D638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 83 | MPa | ASTM D790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2310 | MPa | ASTM D790 | |
| Tensile Stress, yield, 50 mm/min | 52 | MPa | *** 527 | |
| Tensile Stress, break, 50 mm/min | 46 | MPa | *** 527 | |
| Tensile Strain, yield, 50 mm/min | 4.7 | % | *** 527 | |
| Tensile Strain, break, 50 mm/min | 102 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2180 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 81 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2140 | MPa | *** 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 583 | J/m | ASTM D256 | |
| Izod Impact, notched, 0°C | 507 | J/m | ASTM D256 | |
| Izod Impact, notched, -30°C | 425 | J/m | ASTM D256 | |
| Instrumented Dart Impact Energy @ peak, 23°C | 51 | J | ASTM D3763 | |
| Instrumented Dart Impact Total Energy, 23°C | 59 | J | ASTM D3763 | |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 40 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 37 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 56 | kJ/m? | *** 179/1eA | |
| THERMAL | ||||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 128 | °C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 | |
| Vicat Softening Temp, Rate B/50 | 121 | °C | *** 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 128 | °C | *** 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 103 | °C | *** 75/Af | |
| PHYSICAL | ||||
| Melt Flow Rate, 260°C/5.0 kgf | 17 | g/10 min | ASTM D1238 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 18 | cm?/10 min | *** 1133 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 100-110 | °C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260-290 | °C | ||
| Nozzle Temperature | 240-280 | °C | ||
| Front - Zone 3 Temperature | 250-290 | °C | ||
| Middle - Zone 2 Temperature | 250-290 | °C | ||
| Rear - Zone 1 Temperature | 230-260 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 60-90 | °C |