Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.EuropeAsiaAmericas
下载文件技术数据
比较
EUROPE
ASIA
AMERICAS
| Revision: 15/08/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yield, 50 mm/min | 50 | MPa | *** 527 | |
| Tensile Strain, break, 50 mm/min | 120 | % | *** 527 | |
| Tensile Modulus, 1 mm/min | 2050 | MPa | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | *** 178 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m? | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 30 | kJ/m? | *** 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 20 | kJ/m? | *** 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m? | *** 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m? | *** 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | *** 179/1eU | |
| THERMAL | ||||
| Thermal Conductivity | 0.2 | W/m-°C | *** 8302 | |
| CTE, 23°C to 80°C, flow | 9.E-05 | 1/°C | *** 11359-2 | |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | *** 11359-2 | |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 155 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/50 | 120 | °C | *** 306 | |
| Vicat Softening Temp, Rate B/120 | 125 | °C | *** 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 105 | °C | *** 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 82 | °C | *** 75/Ae | |
| Relative Temp Index, Elec | 75 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.7-1.1 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.8-1.1 | % | SABIC method | |
| Density | 1.22 | g/cm? | *** 1183 | |
| Water Absorption, (23°C/saturated) | 0.5 | % | *** 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | *** 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 15 | cm?/10 min | *** 1133 | |
| ELECTRICAL | ||||
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card Link | E45329-236626 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-100 | °C | ||
| Drying Time | 2-4 | Hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 255-270 | °C | ||
| Nozzle Temperature | 250-265 | °C | ||
| Front - Zone 3 Temperature | 250-270 | °C | ||
| Middle - Zone 2 Temperature | 240-265 | °C | ||
| Rear - Zone 1 Temperature | 230-250 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-80 | °C |