VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.AsiaAmericas
下载文件技术数据
比较
ASIA
AMERICAS
| Revision: 15/08/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yield | 96 | MPa | SABIC - Japan Method | |
| Tensile Strain, break | 5-5 | % | SABIC - Japan Method | |
| Flexural Stress | 128 | MPa | ASTM D790 | |
| Flexural Modulus | 6080 | MPa | ASTM D790 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 137 | J/m | ASTM D256 | |
| THERMAL | ||||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 | |
| CTE, -30°C to 30°C | 0.00003-0.00003 | 1/°C | TMA | |
| PHYSICAL | ||||
| Specific Gravity | 1.42 | - | ASTM D792 | |
| Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 | |
| Mold Shrinkage, flow, 3.2 mm | 0.2-0.4 | % | SABIC method | |
| Mold Shrinkage, flow, 6.4 mm | 0.6-0.8 | % | SABIC method | |
| ELECTRICAL | ||||
| Surface Resistivity | 1.E+16 | Ω | ASTM D257 | |
| Relative Permittivity, 50/60 Hz | 3 | - | ASTM D150 |