CELANEX? 2404MT
PBT
典型数据
加工方法
注塑
供货形式
粒料
添加剂
脱模助剂
产品
unfilled medium flow, PTFE filled grade, with improved sliding, low friction and wear, for use in medical applications
Celanex 2404MT is an unreinforced, tribologically-modified and nucleated, medium flow PBT grade for injection molding processing.
Celanex 2404MT is a special grade developed for medical industry applications and complies with:
CFR 21 (177.1660) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 10047 (US) / 10033 (EU)) and the Device Master File (MAF 443 (US) / 1078 (EU))
the corresponding EU and national registry regulatory requirements
biocompatibility in tests corresponding to USP 23 Class VI/*** 10993
low residual monomers
no animal products
总说明
Value
测试方法
制品标识码
> (PBT+PTFE) <
*** 11469
流变性能
Value
单位
测试方法
熔体体积流动速度, MVR
21
cm?/10min
*** 1133
温度
250
°C
负荷
2.16
kg
模塑收缩率, 平行
1.7 - 2.1
%
*** 294-4, 2577
模塑收缩率, 垂直
1.8
%
*** 294-4, 2577
机械性能
Value
单位
测试方法
拉伸模量
2600
MPa
*** 527-1/-2
屈服应力, 50mm/min
56
MPa
*** 527-1/-2
屈服伸长率, 50mm/min
7
%
*** 527-1/-2
名义断裂伸长率
19
%
*** 527-1/-2
剪切模量
964
MPa
*** 6721
简支梁缺口冲击强度, +23°C
3.3
kJ/m?
*** 179/1eA
热性能
Value
单位
测试方法
熔融温度, 10°C/min
225
°C
*** 11357-1/-3
玻璃化转变温度, 10°C/min
60
°C
*** 11357-1/-3
热变形温度, 1.80 MPa
55
°C
*** 75-1/-2
维卡软化温度, 50°C/h 50N
190
°C
*** 306
电性能
Value
单位
测试方法
相对漏电起痕指数
PLC 0
PLC
UL 746A
其它性能
Value
单位
测试方法
吸湿性, 2mm
0.2
%
类似*** 62
密度
1340
kg/m?
*** 1183
注塑
Value
单位
测试方法
干燥温度
120 - 130
°C
干燥时间，除湿干燥机
4
h
加工前水分含量
0.02
%
***熔体温度
255
°C
Internal